Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials by Four-Point Bending ASTM D6272
Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials
Flexural Properties by Four-Point Bending ASTM D6272 Scope:
The Flexural test ASTM D6272 measures the force required to bend a plastic beam under a four point loading system. This test method is used for reinforced or unreinforced materials including high modulus composites and for materials that do not fail within the limits of ASTM D790 (a three point loading test). The difference between the three point and the four point flexural tests is the location of the bending moment. The four point bending method allows for uniform distribution between the two loading noses, while the three point bending method’s stress is located under the loading nose.
Since the flexural properties of many materials can vary depending on temperature, rate of strain and specimen thickness, it may be appropriate to test materials at varied parameters.
Test Procedure: For the four point flexural test, the specimen lies on a span and stress is uniformly distributed between the loading noses. There are two procedures within the ASTM D6272 method. Procedure A is followed for materials with smaller deflection and for measuring modulus. Procedure B is followed for materials with larger deflections and used for measuring strength. Polymer materials specifications may also be followed. Support span-to-depth ratios are dependent on material type and thickness. Load span to support span can be a ratio of 1 to 2 or 1 to 3.
Elevated or Reduced Temperature Test Procedure:
A thermal chamber is installed on the Universal Testing Machine. The chamber is designed to allow the test mounts from the base and crosshead of the Tester to pass through the top and bottom of the chamber. Standard test fixtures are installed inside the chamber, and testing is conducted inside the controlled thermal environment the same as it would be at ambient temperature. The chamber has internal electric heaters for elevated temperatures and uses external carbon dioxide gas as a coolant for reduced temperatures.
ASTM D6272 outlines specimen sizes for specimens with thickness less than 1/16 inch, thickness greater than 1/16 inch, laminate thermosetting sheet, molded materials and high-strength reinforced composites. Five specimens are typically tested. For anisotropic materials, flatwise and edgewise specimens may be tested.
- Flexural Strength
- Flexural Yield Strength
- Flexural Offset Yield Strength
- Stress at Strain
- Tangent Modulus of Elasticity
- Secant Modulus of Elasticity
Equipment Used: Universal Testing Machine; Four Point Flexural Test Fixture
**Please note that this test description is intentionally generic in nature and aimed at providing a descriptive summary to enhance test understanding.
Need help or have a question?
- Wilton UK:
- +44 1642 435 788
- +31 88 126 8888
- +65 6805 4800
- 0800 5855888
- +49 711 27311 152
- +41 61 686 4800
- 01 800 5468 3783
- +52 55 5091 2150
- +55 11 2322 8033
- +61 1300 046 837
- +91 22 4245 0207